Tungsten Alloy Cylinder

Time : 2024-06-21Hits : 642

Tungsten alloy cylinders are the superior product for balancing and weighting cars. Tungsten is 3.2 times heavier than no-lead weighting material often used on cars, thus it enables tremendous flexibility in the design of the car. Incremental it contains five 1/2 ounce cylinders, one 1/4 ounce cylinders, and two 1/8 ounce cylinders. Using the incremental cylinders, you can achieve any weight between 0 and 3 ounces in 1/8 ounce increments.

Compared with square tungsten bar, tungsten alloy cylinder is more popular because machining and production is easier. It is easier to take it from the mold after press which means less damage. Moreover, it is more suitable for further machining.

Applications for Tungsten Alloy Cylinders

Tungsten alloy cylinders can be easily used for car weighting by drilling one or more 25/64" or larger diameter holes into the block and then inserting the desired number of cylinders. The hole can then be plugged with a piece of 3/8 inch dowel rod. The product also is manufactured as the parts of military defense, extrusion die, various counterweights, such as yacht counterweights, vehicle counterweights, airplane counterweights, helicopter counterweights, boat counterweights, tank counterweights, etc.

Usually, tungsten alloy cylinder could be manufactured as the parts for military applications, extrusion die and various kinds of counterweights.

Tungsten Alloy Cylinder

Specification:

1.2.0-100.0mm

2.50-1000mm

3.16.5-18.75g/cm3

4.85-99%，W-Ni-Fe，W-Ni-Cu

①Diameter: 2.0-100.0mm

②Length: 50-1000mm

③Density: 16.5-18.75 g/cm3

④Composition: W content: 85-99%, W-Ni-Fe, W-Ni-Cu

⑤Surface: Sintered surface, Forged surface, Ground surface

Tungsten Alloy Cylinder Data Sheet

Grades	g/cm³ Density g/cm³	HRC Hardness HRC	MPaTensile	Elongation%	MJ/m² Impact
W273	17.10±0.15	≥23	≥900	≥24	≥1.30
W263	17.25±0.15	≥23	≥900	≥23	≥1.20
W253	17.40±0.15	≥24	≥900	≥22	≥1.10
W243	17.60±0.15	≥24	≥920	≥20	≥0.90
W232	18.10±0.15	≥25	≥920	≥14	≥0.45
W231	18.30±0.15	≥26	≥920	≥12	≥0.30
W221	18.50±0.15	≥27	≥920	≥10	≥0.22
WNiCu	16.00-18.50	≥22	≥450	2-8